Heat Shrinkable Tubing
 
 
 
Halogen free, Flame retardant, environmental-friendly,Heat shrinkable Insulating polyolefin tubing
 
             
             
             
 

Flame Retardant

Shrink Ratio 2:1 DownLoad
 
Features
  • Halogen free, environmental-friendly
  • Shrink ratio (Radial change): 2:1, shrink ratio in longitudinal¡Ü5%
  • Min. shrink temperature: 70 ¡æ; Full recovery temperature: 110 ¡æ
  • Continuous Operating Temperature: -30 ¡æ~125 ¡æ
    Specifications / Approvals: UL 224 , CSA22.2
  • Meet SONY STANDARD SS-00259 requirement
  • Flame-retardant: Pass VW-1 flame test
  • Excellent chemical and solvent resistance properties
 
 
Application
Halogen free, Flame retardant, Heat shrinkable polyolefin tubing, typically used where halogen, PBBEs, PBBOs or PBBs are forbidden and environmental-friendly is requirement. Widely used in fields of automotive, electronics, military, marine and aerospace..
 
 
Technical Data
Item   Property  
Requirements
  
Typical Performance
 
Test Method
Mechanical   Tensile Strength  
¡Ý10.4MPa
  
13MPa
 
UL 224
  Ultimate elongation  
¡Ý200%
  
450%
  
UL 224
  Tensile Strength after Heat Aging (158 ¡æ /168hrs)  
¡Ý7.3MPa
  
11MPa
 
UL 224
  Ultimate elongation after Heat Aging (158 ¡æ /168hrs)  
¡Ý100%
 
360%
  
UL 224
  Maximum secant modulus  
¡Ü173 MPa (25 000 psi)
 
¡Ü173 MPa (25 000 psi)
 
UL 224
  Heat shock (250 ¡æ /4hrs)  
No cracking
  
Pass
 
UL 224
  Cold bend (-30 ¡æ /1hr)  
No cracking
  
Pass
 
UL 224
Electrical   Dielectric withstand voltage  
AC.2.5kV/60seconds
 
Pass
 
UL 224
  Dielectric breakdown voltage  
>25kV/mm
  
Pass
 
UL 224
  Volume Resistivity  
>1014¦¸.cm
 
>1015¦¸.cm
 
ASTM D 257
Chemical   Copper Corrosion (158 ¡æ /168hrs)  
No Corrosion
 
Pass
 
UL 224
  Stability  
Elongation>100%
 
>200%
 
UL 224
  Flammability  
Pass
 
Pass
 
UL VW-1
 
 
Dimensions
ORDER
REF.Size
Inside Diameter
Recovered Wall Thickness
After Heating(NOM)
Minimum Expanded as Supplied
Maximum Recovered After Heating
mm
inch
mm
inch
mm
inch
mm
inch
0.8
3/64
0.90
0.035
0.40
0.016
0.18
0.007
1.0
1/16
1.30
0.051
0.50
0.020
0.18
0.007
1.5
3/32
1.80
0.071
0.75
0.03 0
0.20
0.008
2.0
7/64
2.30
0.090
1.00
0.039
0.22
0.009
2.5
1/8
2.80
0.110
1.25
0.049
0.25
0.010
3.0
9/64
3.30
0.130
1.50
0.059
0.25
0.01 0
3.5
5/32
3.80
0.149
1.75
0.069
0.25
0.01 0
4.0
3/16
4.30
0.169
2.00
0.079
0.25
0.01 0
4.5
13/64
5.00
0.197
2.25
0.089
0.25
0.01 0
5.0
7/32
5.30
0.208
2.50
0.098
0.25
0.01 0
6.0
1/4
6.30
0.248
3.00
0.118
0.25
0.01 0
7.0
19/64
7.20
0.273
3.50
0.138
0.25
0.01 0
8.0
11/32
8.10
0.317
4.00
0.157
0.3 0
0.012
9.0
3/8
9.10
0.358
4.50
0.177
0.3 0
0.012
10.0
13/32
10.10
0.397
5.00
0.197
0.3 0
0.012
11.0
29/64
11.10
0.437
5.50
0.217
0.6 0
0.024
12.0
1/ 2
12.10
0.476
6.00
0.236
0.6 0
0.024
13.0
17/32
13.10
0.515
6.50
0.256
0.6 0
0.024
14.0
37/64
14.20
0.559
7.00
0.276
0.6 0
0.024
15.0
39/64
15.20
0.598
7.50
0.295
0.65
0.026
16.0
21/32
16.30
0.641
8.00
0.315
0.65
0.026
18.0
3/4
18.30
0.720
9.00
0.354
0.75
0.03 0
20.0
53/64
20.70
0.815
10.00
0.394
0.8 0
0.031
22.0
29/32
22.70
0.893
11.00
0.433
0.8 0
0.031
25.0
1
26.00
1.023
12.50
0.492
0.9 0
0.035
28.0
17/64
29.00
1.141
14.00
0.551
0.9 0
0.035
30.0
11/4
31.00
1.220
15.00
0.591
0.9 0
0.035