| Transparent, High
Temperature, Polyvinylidene Fluoride(PVDF)
Heat Shrinkable Tubing |
|
| |
|
|
| |
| Features |
- High temperature, highly
flame retardant
- Tough, semirigid, high
withstand to abrasion and cut-through
- Excellent chemical and
solvent resistance
- 2:1 shrink ratio (Radial
change), shrink ratio in longitudinal¡Ü10%
- Min. shrink temperature:
155 ¡æ; Full recovery temperature: 175
¡æ
- Continuous Operating Temperature:
-55 ¡æ~175 ¡æ
|
| |
|
|
| |
Application
Especially suitable for applications requiring
high temperature performance, outstanding
abrasion resistance and cut-through resistance,
or superior chemical and solvent properties.
Provides electrical insulation and strain
relief of multipin connectors and solder joints.
Ideal for applications that require dense
packing of components or visual inspection
of covered components. |
| |
|
|
| |
| Technical Data |
| Item |
|
Property |
|
Requirements |
|
Typical
Performance |
|
Test
Method |
|
|
|
|
|
|
|
|
|
|
|
| Mechanical |
|
Tensile Strength
|
|
¡Ý10.4MPa |
|
40MPa
|
|
ASTM
D2671 |
|
|
|
|
|
|
|
|
| |
Ultimate
elongation |
|
¡Ý200% |
|
450% |
|
ASTM
D2671 |
|
|
|
|
|
|
|
|
| |
Ultimate
elongation after Heat Aging (220 ¡æ /168hrs)
|
|
¡Ý100%
|
|
120% |
|
ASTM
D2671 |
|
|
|
|
|
|
|
|
| |
Heat shock
(300 ¡æ /4hrs) |
|
|
|
no
dripping |
|
ASTM
D2671 |
|
|
| |
Low Temperature
Flexibility (-40 ¡æ /4hr) |
|
|
|
Pass
|
|
ASTM
D2671 |
|
| Electrical |
|
Dielectric
Strength |
|
>25kV/mm |
|
33kV/mm |
|
ASTM
D2671 |
|
|
| |
Volume Resistivity
|
|
>1013¦¸.cm
|
|
>1014¦¸.cm
|
|
ASTM
D 257 |
|
| Chemical |
|
Copper Corrosion
(220 ¡æ /168hrs) |
|
No
Corrosion |
|
Pass
|
|
ASTM
D2671 |
|
|
| |
Stability
(121 ¡æ /168hrs) |
|
Elongation>100%
|
|
pass |
|
UL
224 |
|
|
| |
Flammability
|
|
|
|
Highly
Flame Retardant |
|
ASTM
D2671 |
|
|
|
|
|
|
|
|
| |
Water Absorption
|
|
<0.5%
|
|
<0.5%
|
|
ASTM
D570 |
|
|
| |
|
| |
| Dimensions |
|
ORDER
REF.Size |
Inside
Diameter |
Recovered
Wall Thickness
After Heating(NOM) |
|
Minimum
Expanded as Supplied |
Maximum
Recovered After Heating |
|
mm |
inch |
mm |
inch |
mm |
inch |
mm |
inch |
|
|
|
|
|
|
|
|
1.2 |
3/64
|
1.20 |
0.047 |
0.60 |
0.024 |
0.25¡À0.1
|
0.010¡À0.004
|
|
1.6 |
1/16
|
1.60 |
0.063 |
0.80 |
0.032 |
0.25¡À0.1
|
0.010¡À0.004
|
|
2.4 |
3/32
|
2.40 |
0.094 |
1.20 |
0.047 |
0.25¡À0.1
|
0.010¡À0.004
|
|
3.2 |
1/8
|
3.20 |
0.126 |
1.60 |
0.063 |
0.25¡À0.1
|
0.010¡À0.004
|
|
4.8 |
3/16
|
4.80 |
0.189 |
2.40 |
0.095 |
0.30¡À0.1
|
0.012¡À0.004
|
|
6.4 |
1/4
|
6.40 |
0.252 |
3.20 |
0.126 |
0.30¡À0.1
|
0.012¡À0.004
|
|
9.6 |
3/8
|
9.60 |
0.378 |
4.80 |
0.189 |
0.30¡À0.1
|
0.012¡À0.004
|
|
12.8 |
1/2
|
12.80 |
0.504 |
6.40 |
0.252 |
0.30¡À0.1
|
0.012¡À0.004
|
|
19 |
3/4
|
19.00 |
0.748 |
9.50 |
0.374 |
0.40¡À0.1
|
0.016¡À0.004
|
|
25.4 |
1 |
25.40 |
1.000 |
12.70 |
0.500 |
0.50¡À0.1
|
0.020¡À0.004
|
|
38 |
1
1/2 |
38.00 |
1.496 |
19.00 |
0.748 |
0.50¡À0.1
|
0.020¡À0.004
|
|
|
| |
|
|
|
|
| |
|
| |